Pengaruh teknik dan waktu pencampuran pada pembuatan lembaran cocodust berkaret untuk bahan peredam suara

Arum Yuniari

Abstract


Research about cocodust rubber sheet production for sounds absorbent material was determined to improve mixing technology between cocodust and latex compound so there can be gained effective mixing technology. There are 2 methods regarding to mixing technology which were A method and B method with time variation method between 2, 3 until 4 minute respectively time. A method was cocodust with sieved by 50 mesh siefter mixed with water (ratio time between cocodust and water 1:3) and subsequently cocodust was mixed with latex compound. While B method was mixing latex compound and water (the mixture consisting of 3 part of water and 1 part of latex) and the final product was blended. The result show that A method with time variation of 2 – 3 minutes was the best effective mixing method. The result of a method can be easily implemented, having homogeny compound and good product performance, which was characterized by mass density 0,40 g/cm3, water content 7,29 – 7,57%, flexibility strength 2,87 – 4,05 kg/cm2, vertical tensile strength 1,97 – 3,12 kg/cm2, ability to be nailed 4,95 – 5,92 kg, thickness grows 7,5 – 8,28% and sound absorption coefficient at the frequency 500 Hz was 0,70.

 Keywords: cocodust, latex compound, sound absorbent.

 

ABSTRAK

Penelitian tentang pembuatan lembaran cocodust berkaret untuk bahan peredam suara bertujuan untuk menyempurnakan teknik pencampuran antara cocodust dengan bahan perekat (kompon lateks) agar diperoleh metode pencampuran yang efektif. Teknik pencampuran dilakukan dengan 2 metode yaitu metode A dan metode B dengan variasi waktu pencampuran berturut-turut 2, 3 dan 4 menit untuk masing-masing metode. Metode A menggunakan cocodust diameter 50 mesh dibasahi dengna air lebih dahulu (perbandingan cocodust : air adalah 1 : 3), selanjutnya cocodust dicampur dengan kompon lateks. Metode B menggunakan kompon lateks yang diencerkan dahulu dengan air (3 bagian air dan 1 bagian lateks) selanjutnya dicampur dengan cocodust lolos saring 50 mesh. Hasil penelitian menunjukkan bahwa metode pencampuran A, dengan variasi waktu pencampuran 2 – 3 menit merupakan metode pencampuran yang efektif mudah dilakukan, menghasilkan campuran homogen tanpa ada penggumpalan, kenampakan produk cukup bagus dengan sifat fisika kerapatan 0,40 g/cm3, kadar air 7,29 – 7,57%, kuat lentur 2,87 – 4,05 kg/cm2, kuat tarik tegak lurus permukaan 1,97 -3,12 kg/cm2, kuat pegang sekrup 4,95 – 5,92 kg, pengembangan tebal 7,5 – 8,28% dan koefisien penyerapan suara pada frekuensi 500 Hz sebesar 0,70.

 Kata kunci: cocodust, kompon lateks, peredam suara.


Full Text:

PDF

References


Arizal, R. (1994). Pengetahuan Dasar Elastomer. Bogor: Balai Penelitian Teknologi Karet.

Bsn (Badan Standardisasi Nasional. (1996). Standar Nasional Indonesia SNI 2105:1996: Mutu Papan Partikel. Jakarta, Indonesia: BSN.

Free, E.E. (1972). The Book of Popular Science: Progress in Accoustics: Volume 8 (pp. 45-46). Canada: The Grolier Society Inc.

JIS (Japan International Standard). (1988). JIS 1405: Method of Test for Sound Absorption of Accoustical Materials by The Tube Method, Japan: JIS.

Knauss, H.P. (1972). The Book of Popular Science: Analysis of Sound: Volume 5 (pp. 114-115,122). Canada: The Grolier Society Inc.

Kusnata. (1975). Pedoman Praktek Pembuatan Barang Karet dari Lateks. Bogor: Balai Penelitian Teknologi Karet.

Maloney, T. (1977). Modern particleboard and dry-process fiberboard manufacturing. San Fransico: Miller Freeman Publication. Inc.,

Ola, A. L., & Roeroe, H. J. M. (1977). Pengaruh Kekuatan Press Cetak terhadap Mutu Papan Partisi dari Serbuk Sabut Kelapa. Majalah BIMA, 11, 10-15.

Osman, T., Mc. Corry, V., Cooper, C., Innes, B., & Sullings, J. (1980). New Encyclopedia of Science: Accoustic: Volume 1 (pp. 20-23). Cordorbe: Orbis Publishing Ltd.

Setyowati, P., Yuniari, A., Rochani, S., & Surip, H. (2004). Pemanfaatan Limbah Pertanian Serbuk Sabut Kelapa (Cocodust) Untuk Pembuatan Komposit Karet. Yogyakarta: Balai Besar Kulit Karet dan Plastik.

Setyowati, P., Yuniari, A., Rochani, S., & Surip, H. (2008). Pengembanagan Lembaran Cocodust Berkaret untuk Bahan Peredam Suara. Yogyakarta: Balai Besar Kulit Karet dan Plastik.

Sitorus, H., & Widardo, S.H. (1998). Pengaruh Jenis Perekat pada Pembuatan Briket Serbuk Sabut Kelapa, Majalah BIMA, 11, 1-9.

Soedarsan, A. (1985). Petunjuk Pembuatan Barang dari Karet Alam. Bogor: Balai Penelitian Teknologi Karet.

Thampan, P. K. (1981). Handbook on coconut palm. Handbook on coconut palm. New Delhi: Oxford & IBH Publishing Co.

Zulkifli, R., Nor, M. J. M., Ismail, A. R., Nuawi, M. Z., Abdullah, S., Tahir, M. F. M., & Ab Rahman, M. N. (2009). Comparison of acoustic properties between coir fibre and oil palm fibre. European Journal of Scientific Research, 33(1), 144-152.




DOI: http://dx.doi.org/10.20543/mkkp.v25i1.227

Refbacks

  • There are currently no refbacks.


Copyright (c) 2015 Arum Yuniari

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

 

MKKP indexed by:

Cover Page Cover Page     Cover Page    Cover Page     Cover Page     Cover Page     Cover Page     Cover Page     Cover Page     Cover Page    Cover Page    Cover Page    Cover Page     Cover Page     Cover Page   Cover Page   Cover Page   Cover Page   Cover Page              

 

 

 

Free counters!