Sintesis dan Karakterisasi Membran Selulosa Asetat dari Tandan Kosong Kelapa Sawit (Synthesis and Characterization of Cellulose Acetate Membranes from Oil Palm Empty Fruit Bunches)

Rina Apriani, Taufiqur Rohman, Kamilia Mustikasari

Abstract


The research of synthesis and characterization of cellulose acetate membranes from
oil palm empty fruit bunches (OPEFB) had been done. The purpose of this research is to
find out the characteristics of the cellulose acetate membrane from cellulose acetate of
OPEFB. The cellulose acetate membrane was prepared using the cellulose acetate (CA)
and chloroform as solvent in the ratio 1:6, and the variations of polietilena glycol (PEG) as
additives were 10%, 20%, and 30% w/w. Membrane characterization was done in
permeability (flux), permselektivitas (rejection), and membrane morphology. The test was
performed on water, T-­70;; 1% w/v and T-­500;; 1% w/v dextran solution. The results
showed that cellulose acetate membrane had the best characteristic in the addition of
PEG/S 10% w/w. The permeability was 55.54 L/m2hour in water, 18.48 L/m2hour for
dextran T-­70 and 5.14 L/m2hour for dextran T-­500. The perm selectivity was 67.24% for
dextran T-­70 and 79.46% for dextran T-­500. The SEM (Scanning Electron Microscope)
analysis on membrane pore showed that the distribution of pore sizes is fine.

Keywords : membrane, cellulose acetate, oil palm empty fruit bunches


Keywords


membrane; cellulose acetate; oil palm empty fruit bunches

Full Text:

PDF

References


Apriani, R. (2017). Pemanfaatan Selulosa Tandan Kosong Kelapa Sawit (TKKS) sebagai Bahan Pembuatan Membran Selulosa Asetat (Skripsi). Universitas Lambung Mangkurat.

Aprilia, S., & Amin, A. (2011). Sintesis dan Karakterisasi Membran untuk Proses Ultrafiltrasi. Jurnal Rekayasa Kimia dan Lingkungan, 8(2), 84–88.

Apriani, R. (2017). Pemanfaatan Selulosa Tandan Kosong Kelapa Sawit (TKKS) sebagai Bahan Pembuatan Membran Selulosa Asetat (Skripsi). Universitas Lambung Mangkurat.

Aprilia, S., & Amin, A. (2011). Sintesis dan Karakterisasi Membran untuk Proses Ultrafiltrasi. Jurnal Rekayasa Kimia dan Lingkungan, 8(2), 84–88.

Armedi, J., & Angela, R. (2011). Sintesis dan Karakterisasi Membran Hibrid PMMA/TEOT : Pengaruh Konsentrasi Polimer (pp. 1–7).

Ayusnika, R., & Gunawan, H. (2014). Membran Komposit Ca-Ps Pemisah Limbah Batik (Rhodamine B) Dengan “Dead-End” Membrane Reactor. Jurnal Pharmacy, 11(02), 200–214.

Bahmid, N. A. (2014). Pengembangan Nanofiber Selulosa Asetat dari Selulosa Tandan Kosong Kelapa Sawit Untuk Pembuatan Bioplastik (Thesis). Institut Pertanian Bogor.

CM.Rosnelly, Darmadi, S. (2013). Effect of Dope Solution Temperature on Characteristic and Performance of Cellulose Diacetate Membrane Based on Cellulose of Sengon Wood (Paraserianthes falcataria sp). In Journal on Advanced Science Engineering Information Technology, 3(2), 15–18.

Fuadi, A. M., & Pranoto, H. (2016). Pemanfaatan Limbah Tandan Kosong Kelapa Sawit Sebagai Bahan Baku Pembuatan Glukosa. Jurnal Chemica, 3(1), 1–5.

Gaol, M. R. L. L., Sitorus, R., S, Y., Surya, I., & Manurung, R. (2013). Pembuatan Selulosa Asetat dari α-Selulosa Tandan Kosong Kelapa Sawit. Jurnal Teknik Kimia, 2(3), 33–39.

Iriyanti, A. (2016). Sintesis Membran Elektrolit Selulosa Asetat Dari Daun Pandan Laut (Pandanus Tectorius) Dengan Pemlastis Dimetil Ftalat Untuk Aplikasi Baterai Ion Litium (Skripsi). Universitas Negeri Yogyakarta.

Lindu, M., Puspitasari, T., & Ismi, E. (2010). Sintesis dan Karakterisasi Selulosa Asetat dar Nata de Coco Sebagai Bahan Baku Membran Ultrafiltrasi. Jurnal Sains Materi Indonesia, 12(1), 17–23.

Djuned, F.M., Asad, M., Ibrahim, M. N. M., & Daud, W. R. W. (2014). Synthesis and Characterization of Cellulose Acetate from TCF Oil Palm Empty Fruit Bunch Pulp. Bioresources. 9(3), 4710-4721.

Mulder, M. (1996). Basic Principle of Membrane Technology. Netherland: Kluwer Academic Publisher.

Pinnata, R., & Damayanti, A. (2012). Pemanfaatan Selulosa Asetat Eceng Gondok Sebagai Bahan Baku Pembuatan Membran Untuk Desalinasi (Skripsi). Institut Teknologi Sepuluh Nopember.

Rohman, T., Baroroh, U., & Utami, L. (2009). Pengaruh Konsentrasi Kitosan terhadap Karakter Membran Kitosan. Jurnal Sains Dan Terapan Kimia, 2(1), 14–24.

Rosnelly, C. (2010). Perancangan Proses Pembuatan Membran Ultrafiltrasi Selulosa Asetat secara Inversi Fasa dari Selulosa Pulp Kayu Sengon (Paraserianthes falcataria) (Thesis). Institut Pertanian Bogor.

Wardani, A. (2013). Pengaruh Aditif pada Pembuatan Membran Ultrafiltrasi Berbasis Polisulfon untuk Pemurnian Air Gambut (Skripsi). Institut Teknologi Bandung.




DOI: http://dx.doi.org/10.24111/jrihh.v9i2.3305

Refbacks

  • There are currently no refbacks.




JRIHH INDEXED BY :

     
       


Published by BARISTAND INDUSTRI BANJARBARU (E-ISSN: 2503-0779 dan P-ISSN : 2086-1400).

 Creative Commons License