PAPAN PARTIKEL DARI SERBUK KAYU DAN LIMBAH PENYULINGAN KULIT KAYU GEMOR (Alseodaphne spp.)

Budi Tri Cahyana

Abstract


Utilization of gemor bark (Alseodaphne spp) distillation waste for particle board had been carried out. The aim of this research was physical mechanical from wood sawdust waste mixed with gemor bark distillation waste which properties physically and mechanically meet quality requirements. The raw materials used were sawdust mixed with gemor bark distillation waste which mashed16 mesh and the adhesive used were starch and PVAC. Composition variety of the mixture of wood sawdust waste particles and gemor bark distillation waste particle 50%: 50%, 60%: 40%., 70%: 30% with 5% adhesive. The results showed that highest average of modulus of rupture (27,55 kg/cm2) was obtained in 70% : 30% comparison of  sawdust and gemor bark distillation waste with starch adhesive (a3b1) and the density average was 0.75 gr/cm3. The highest average of modulus of elasticity (351,50 kg/cm2) was in composition of 60%: 40% with starch adhesive (a2b1) and the density average was 0.69 gr/cm3. The highest average of tensile strength (4,11 kg/cm2) was obtained in composition of 50%: 50% with starch adhesive and the density average was  0.79 gr/cm3.

Keywords: sawdust wood, distillation waste, gemor bark, particle board


Full Text:

PDF

References


Anonim, 2007. www.tentangkayu.com/ 2007/12/limbah-dari-industri-kayu.html. Diaskes tanggal 20 Juni 2011.

Abdurachman dan Nurwati Hadjib. 2011. Sifat Papan Partikel dari Kayu Kulit Manis (Cinnamomum burmanii BL). Bogor : Pusat Penelitian dan Pengembangan Keteknikan Kehutanan dan Pengolahan Hasil Hutan Bogor.

Badan Standardisasi Nasional.2006. Papan Partikel. Standar Nasional Indonesia (SNI) 03-2105-2006.

Dinas Kehutanan Propinsi Kalimantan Selatan. 2003. Statistik Kehutanan 2002 Propinsi Kalimantan Selatan.

Departemen Kehutanan 2004. Pemanfaatan Limbah Kayu. Bahan Ekspos dengan Menteri Kehutanan. Bogor : Pusat Penelitian dan Pengembangan Teknologi Hasil Hutan. Badan Litbang Departemen Kehutanan.

Djoko Purwanto, 2011. Pembuatan Balok dan Papan dari Limbah Industri Kayu. Jurnal Riset Industri. Baristand Industri Banjarbaru. 5 (1): 13-20.2011.

Ema Ratri Kartika J. W. 2011. Kualitas Papan Partikel Dari Log Diameter Kecil. Bogor : Fakultas Kehutanan Institut Pertanian Bogor.

Jufriah, Wagiman, S., Masrinah. 2007. Sifat Fisika dan Mekanika Papan Partikel dari Batang Sawit (Elaeis Gueneensis, Jaeq) dengan Variasi Temperatur Kempa Panas. RIMBA Kalimantan Fakultas Kehutanan Universitas Mulawarman. 2 (2) : 106-114.2007.

Haygreen, J.G. dan J.L. Bowyer. 1996. Hasil Hutan dan Ilmu Kayu, Suatu Pengantar. (terjemahan Soetjipto A.H). Yogyakarta : Gadjah Mada University Press.

Paribroto Sutigno. Departemen Kehutanan. 1982. Sifat-sifat Papan Partikel Tiga Jenis Kayu. Jakarta : Duta Rimba.

Paribotro S. dan Adi Santoso. 1991. Pengaruh Penambahan Urea dan Amonium Karbon Pada Perekat UF Terhadap Emisi Formaldehida dan Sifat Fisik Mekanik Papan Partikel. Jurnal Litbang Hasil Hutan. 9 (2).

Santoso, A dan Jasni. 2003. Daya Tahan Garis Rekat LRF pada Kayu Lamina Mani terhadap Serangan Rayap Kayu Kering. J.Ilmu dan Teknologi Kayu Tropis. 1 (1) : 26-37.

S. Ruhendi dan Erwinsyah P. 2011. Sifat Fisik dan Mekanis Papan Partikel dari Batang dan Cabang Kayu Jabon (Anthocephalus cadamba Miq). Jurnal Ilmu dan Tehnologi Hasil Hutan. 4(1) : 14-21. Departemen Hasil Hutan Fakultas Kehutanan IPB. Bogor

Violet Hatta, 2007. Pemanfaatan Hasil Hutan Bukan Kayu Perlu Kearifan. Banjarbaru : Fakultas Kehutanan Universitas Lambung Mangkurat Banjarbaru.




DOI: http://dx.doi.org/10.24111/jrihh.v5i2.1214

Refbacks

  • There are currently no refbacks.




JRIHH INDEXED BY :

       
       


Published by BARISTAND INDUSTRI BANJARBARU (E-ISSN: 2503-0779 dan P-ISSN : 2086-1400).

 Creative Commons License