Pengaruh Kecepatan Pengadukan dan Kehalusan Gambir Serta Variasi Komposisi Terhadap Beberapa Sifat Fisika dalam Pembuatan Tinta Cetak

Hendri Muchtar, Inda Three Anova, Gustri Yeni

Abstract


Ink is a very important element that determines the quality of a printout. One of the potential natural materials that can be used as a raw material for making printing ink is gambier.The objective of this study was to observe the effect of stirring speed and particle size on some physical properties in the printing ink. The ink manufacturing was done in 2 phases, namely the manufacture of color pigment and ink formulation. Pigment ink was made by cleaning the gambier through dilution with hot water, filtration, and precipitation of fitrat. Furthermore the gambier was mashed with particle size variation 40, 60, 80 mesh. The adding saturated FeCl3 compounds in ethanol into the extract gambier slowly with stirring speed 250, 500, 750 rpm for 4 hours. The color of the pigment, viscosity, and the particle size was tested by using the PSA method (particle size analyzer). Manufacture of ink formula with additives propylene glycol 7.5; 10; 12.5 mL and polyethylene glycol 0.1; 0.3; and 0.5 mL for every 30 ml of extract gambier in ethanol. Best pigment was obtained from the use of gambier 60 mesh powder, stirring speed 250 rpm, the smallest pigment particle was 47.54 nm. The best ink formula was using propylene glycol and polyethylene glycol 12.5 mL and 0.5 mL. The characteristics of ink were black colored ink with a density 0.9633 at a temperature of 28-30°C, viscosity 0.9 cP, and surface tension 0.2539 N/m.

ABSTRAK

Tinta merupakan unsur yang sangat penting menentukan kualitas hasil cetakan. Salah satu bahan alam potensial yang dapat dijadikan sebagai bahan baku pembuatan tinta cetak adalah gambir. Penelitian ini bertujuan untuk mengamati pengaruh kecepatan pengadukan dan kehalusan bahan baku gambir terhadap beberapa sifat fisika dalam pembuatan tinta cetak. Pembuatan tinta dilakukan 2 tahap yaitu pembuatan pigmen dan formula tinta. Pigmen tinta dibuat dengan cara membersihkan  gambir melalui pelarutan dengan air panas, penyaringan, dan pengendapan fitrat. Selanjutnya endapan gambir dihaluskan dengan variasi ukuran butiran sebesar  40, 60, 80 mesh. Penambahan senyawa FeCl3  jenuh dalam etanol pada ekstrak gambir dalam 25 ml etanol secara perlahan dengan kecepatan pengadukan bahan sebesar 250, 500, 750 rpm selama 4 jam. Pigmen diuji warna, viskositas, dan ukuran partikel dengan menggunakan metoda PSA (particle size analyzer). Pembuatan formula tinta dengan bahan aditif propilen glikol sebesar 7,5; 10; 12,5 ml dan polietilen glikol 0,1; 0,3; 0,5 ml untuk setiap 30 ml ektrak gambir dalam etanol. Pigmen yang terbaik diperoleh pada pemakaian bubuk gambir 60 mesh, kecepatan pengadukan 250 rpm, ukuran partikel pigmen yang terkecil adalah 47,54 nm. Formula tinta yang terbaik adalah tinta dengan menggunakan propilen glikol 12,5 ml dan polielen glikol 0,5 ml. Karakteristik  tinta bewarna hitam dengan berat jenis pada suhu 28-30oC sebesar 0.9633, viskositas      0,9 cP dan tegangan permukaan 0,2539 N/m.


Keywords


Gambier extract; particle size; printing Ink

Full Text:

PDF

References


Antono, A. and Sebastianus, A. 2013. Pengaruh pemilihan tinta terhadap kualitas cetak dalam industri percetakan koran. Dinamika Teknik, Vol. VII No. 1 Jan., 9-16.

Galuh, S. dan Rahmi, D. 2014. Pembuatan nanopartikel dengan metoda high speed homogenization. Jurnal Litbang Industri, Vol. 3 No. 2, Desember, 67-131.

Gunawan, A., Dessy, E. S. M., Yusuf, T. 2012. Pengaruh waktu pemasakan dan volume larutan pemasak terhadap viskositas pulp dari ampas tebu. Jurnal Teknik Kimia No. 2 Vol. 18, April, 1-8.

Hagerman, A. E. 2002. Condensed tannin structural chemistry. Department of Chemistry and Biochemistry, Miami University, Oxford, OH 45056.

Hidayati, S. 2009. Pengaruh ratio mol, suhu dan lama reaksi terhadap tegangan permukaan dan stabilitas emulsi metil ester sulfonat dari CPO. Jurnal Teknologi Industri dan Hasil Pertanian, Vol. 14 No.1.

Lidiyah. 2011. Peningkatan jumlah nanopartikel kitosan terisi ketoprofen berdasarkan ragam surfaktan dan kondisi ultrasonifikasi. Sekolah Pasca Sarjana IPB Bogor.

Muchtar, H. dan Silfia. 2007. Pemanfaatan gambir sebagai bahan baku tinta stempel. Buletin BIPD Vol. XV No.1, 1-12.

Prasmita, K. 2012. Studi pendahuluan penentuan distribusi ukuran nano partikel logam menggunakan mikroelektroda. FMIPA UI.

Ram Kumar, P., Priya, R., Lakshmi. 2012. Formulation and standardisation of herbal based edible ink. International Journal of Advances in Pharmacy, Biology, and Chemistry, Vol. 1(2), Apr-Jun, ISSN: 2277-4688.

Siva, R. 2007. Status of natural dyes and dye-yielding plants in India. Current Science, Vol. 92 No. 7.

Standar Nasional Indonesia No: 01-3391-2000. Gambir. Badan Standardisasi Nasional Jakarta.

Suhartini, N. 2012. Pemanfaatan arang jerami sebagai bahan dasar pembuatan tinta white board yang ramah lingkungan. Fak. MIPA Universitas Negeri Yogyakarta.

Swider, J. R., Hackley, V. A., Winter, J. 2003. Characterization of chinese Ink in size and suface. Journal of Cultural Heritage 4 (2003) 175-186.

Van, L., Hoegarden, Samuel, T. 1995. New indelible ink formulation. United Stated Patent no.5.449.400.

Wiguna, P., A., Susanto, Said, A., N., Wicaksono, M., R. 2014. Fabrikasi tinta printer berbahan dasar pigmen organik dari sampah. Jurnal Fisika Universitas Negeri Semarang Vol. 4 No. 2 (2014), ISSN 2044-1509.

Yelin, Agustini, L., Rosandy, A. 2010. Sumber bahan pewarna alami sebagai tinta sidik jari pemilu. Puslitbang Hutan dan Konservasi Alam, Departemen Kehutanan, Bogor.




DOI: http://dx.doi.org/10.24960/jli.v5i2.674.131-139

Refbacks

  • There are currently no refbacks.




Copyright (c) 2015 Hendri Muchtar, Inda Three Anova, Gustri Yeni


Our journal indexed by:




Copyright © Baristand Industri Padang, 2015. Powered By OJS

Theme design credited to MEV edited by JLI

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License