KOMBINASI RSS DAN SBR DALAM TEKNOLOGI PEMBUATAN KARET BANTALAN KAKI UNTUK MEBEL

Syamsul Bahri, Aprillena Tornadez Bondan

Abstract


This research was aimed to formulate the rubber step for furniture that meet its technical specification which approach to SNI 06-7032-2004  for Rubber Step of Motor Vehicle . This research used Ribbed Smokes Sheet (RSS) as natural rubber, combined with Styrene Butadiene Rubber (SBR) as synthetic rubber. The formulation of rubber compound used 100, 70, 50 and 30 phr of RSS, and 0, 30, 50 and 70 phr of SBR. The observed parameters for compounds were hardness (ASTM D 2240), tensile strength(ASTM D 412), elongation at break (ASTM D 412), modulus 310% (ASTM D 412), tear resistance (ASTM D 624), abrasion (ASTM D 298), and compression set 25%. The result showed that the best compound was formula III (contained 50 phr of RSS and 50 phr of SBR) with the test result for hardness was 68 Shore A, tensile strength 120 kg/cm2, elongation at break 355 %,  modulus 100% was 25 kg/cm2,  tear resistance 33kg/cm2, abrasion resistance 2,4 mm3/kgm, and compression set 25% value was 23%.

 

Keywords : rubber step, RSS, SBR, furniture


Keywords


rubber step, RSS, SBR, furniture

Full Text:

PDF

References


Blow, C. M. (1971). Rubber technology and manufacture. Loughborough, Butterworths: London: University of Technology.

Fang, Y., M. Zhan, and Wang, Y. (2001). The status of recycling of waste rubber. Materials & Design 22 (2):123-128.

Hamed, G. R. (1992). in Engineering with Rubber, A. N. Gent (Ed.), Hanser, 1st edition. p. 22

Hassan, H. H., Ateia, E., Darwish, N. a., Halim, S. F., & Abd El-Aziz, a. K. (2012). Effect of filler concentration on the physico-mechanical properties of super abrasion furnace black and silica loaded styrene butadiene rubber. Materials and Design, 34, 533–540. http://doi.org/10.1016/j.matdes.2011.05.005

Hao P.T., Ismail H., Hashim A.S. (2001) Study of two types of styrene butadiene rubber in tire tread compounds. Polym Test: 20(5):539–44.

Ismail, H., A. Rusli, and Rashid, A. (2005). Maleated natural rubber as a coupling agent for paper sludge filled natural rubber composites. Polymer Testing, 24(7):856-862.

Kahar, N. 2003. Rapat Ikatan Silang pada Karet Alam yang Divulkanisir. Teknologi Indonesia Jilid VIII. No. 2.

Kanking, S., Niltui, P., Wimolmala, E., and Sombatsompop, N. (2012). Use of bagasse fiber ash as secondary filler in silica on carbon black filled natural rubber compound. Materials Design, 41:74-82.

Lake, G. J. and Lindley, P. B. (1996). in Use of Rubber in Engineering, MacLaren and Sons Ltd., London. p. 67

Liu, C., Shao, Y. and Jia D. (2008). Chemical modified starch reinforced natural rubber composites., 49(8): 2176-2181.

Manal U, Aggarwal K (2001). Studies on rubber–filler interaction in carboxylated nitrile rubber through microhardness measurement. Polym Test; 20(3):305–11.

Nasruddin (2017). Karakteristik Sifat Mekanik Solid Tyre dengan Bahan Pengisi dan Pelunak Berbasis Sumber Daya Alam Lokal. Jurnal Dinamika Penelitian Industri, 28(1).

Pal, K., Rajasekar, R., Kang, D. J., Zhang, Z. X., Pal, S. K., Das, C. K., & Kim, J. K. (2010). Effect of fillers on natural rubber/high styrene rubber blends with nano silica: Morphology and wear. Materials and Design, 31(2), 677–686. http://doi.org/10.1016/j.matdes.2009.08.014

Rahmaniar dan Nuyah. (2016). Pemanfaatan pasir kuarsa sebagai bahan pengisi dalam pembuatan karpet karet. Jurnal Dinamika Penelitian Industri, 27(2).

Rios S, Chicurel R, Del Castillo LF (2001). Potential of particle and fibre reinforcement of tyre tread elasttomers. Mater Des; 22(5):369–72.

Sommer, J. G. (2009). Engineered Rubber Products. Engineered Rubber Products: Introduction to Design, Manufacture and Testing. Munich: Hanser. http://doi.org/10.3139/9783446433441.fm

Susanto, T. (2016). Perbandingan sifat mekanik-fisik vulkanisat SBR dan SBR/NR menggunakan bahan pengisi pati termodifikasi resorcinol formaldehyde. Jurnal Dinamika Penelitian Industri 27(1).

Thomas, J. 2003. Disain kompon. Modul Pelatihan. Balai Penelitian Teknologi Karet Bogor.

Vachlepi, A. dan Suwardin, D. (2015). Kajian Pembuatan Kompon Karet Alam dari Bahan Pengisi Abu Briket Batubara dan Arang Cangkang Sawit. Jurnal Dinamika Penelitian Industri, 26(1).

White, J., & Naskar, K. (2009). Rubber Technologist’s Handbook. (J.

White, S. K. De, & K. Naskar, Eds.) (Vol. 2). United Kingdom: iSmithers Rapra.

Xie W, Hwu JM, Jiang GJ, Buthelezi TM, Pan WP. (2003). A study of the effect of surfactants on the properties of polystyrene - Polymer montmorillonite nanocomposites. Polym Eng Sci, 43:214–22.

Zou H, Xu W, Zhang Q, Fu Q. (2006). Effect of alkylammonium salt on the dispersion and properties of poly(p-phenylene sulfide)/clay nanocomposites via melt intercalation. J Appl Polym Sci, 99:1724–31.




DOI: http://dx.doi.org/10.28959/jdpi.v29i1.3548

Refbacks

  • There are currently no refbacks.


Copyright (c) 2018 Jurnal Dinamika Penelitian Industri

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.