The Use of  Kaolin West Kalimantan as an Extender Pigment In The Manufacture of Emulsion Paint

Uray Lusiana; Heru Agus Cahyanto

doi:10.36974/jbi.v5i2.823

The Use of Kaolin West Kalimantan as an Extender Pigment In The Manufacture of Emulsion Paint

Uray Lusiana, Heru Agus Cahyanto

Abstract

Wall paint emulsion is an emulsion of a mixture of pigments, binders and solvents, and other additives that are used primarily for painting walls. This study was conducted to determine the use of kaolin as a extender pigment West Kalimantan in the manufacture of emulsion paint walls. Kaolin is used combined with titanium dioxide with a percentage of 33% , 42% , 50% , 58% and 67% of the total pigment . The best results are obtained on the addition of 50% kaolin with power caps 29m²/L, density 1.40 g/cm³, fineness of 25microns, dry touch 10 seconds, hard dry 20 minutes, 61.99 wt% total solids, pH 7.21, viscosity 107 KU, resistance to alkali and accelerated weather for 600 hours. This was the best result and has met the quality requirements SNI 3564:2009 of emulsion paint.

Keywords

extender pigment; kaolin; paint

Full Text:

PDF

References

Alabi, F.M. & Omojola, M.O. (2013). Potentials of Nigerian Calcined Kaolin as Paint Pigment. African Journal of Pure and Applied Chemistry, 7(12), 410-417.

Anderson, C.D. & Daniels, E.S., (2003). Emulsion Polymerisation and Latex Applications. Shropshire: Rapra Publishing.

Ashby, M.F., Johnson & Kara. (2009). Materials and Design: The Art and Science of Material Selection in Product Design. Burlington: Butterworth–Heinemann.

Badan Standardisasi Nasional. (2009). Cat Tembok Emulsi. SNI 3564:2009. Jakarta.

Boke, J. W. (2013). Calcium Carbonate Particle Size Effects on Titanium Dioxide Light Scattering in Coatings. Project Report. The Faculty of California Polytechnic State University. San Luis Obispo

Habsari, H.U.S. (2010). Aplikasi Semiotik & Efek Psikologis Tampilan Warna Pada Rumah Minimalis. Riptek, 4(1).

Karakas, F., Pyrgiotakis, G., Çelik, M. S., & Moudgil, B. M. (2011). Na-Bentonite and MgO Mixture as a Thickening Agent for Water-Based Paints. KONA Powder and Particle Journal, 29(0), 96-106.

Kogel, J. E. (Ed.). (2006). Industrial minerals & rocks: commodities, markets, and uses. SME.

Monk, P. (2004). Physical Chemistry: Understanding Our Chemical World. Chichester: John Wiley & Sons.

Nelly, W., Cita & Titin, A. Z. (2012). Analisis Whiteness Kaolin Asal Mandor Pada Variasi Temperatur Pemanasan. POSITRON, 2(2), 15-20.

Nursahan, I. (2005). Inventarisasi dan Evaluasi Mineral Logam di Daerah Kabupaten Bengkayang dan Kabupaten Landak, Provinsi Kalimantan Barat. Subdit Logam, Direktorat Inventarisasi Sumber Daya Mineral.

Painter, P. C., & Coleman M. M. (2009). Essential of Polymer Science and Engineering. Lancaster: DEStech Publications Inc.

Rohm. (2010). The Ingredients of Paint and Their Impact on Paint Properties. Rohm and Haas Paint Quality Institute. http://www.paintquality. com. Diakses tanggal 03 April 2014.

Stewart, D. (2007). Hydrous Kaolin for Decorative Matt Emulsion Paint. European Coating Journal.

DOI: http://dx.doi.org/10.36974/jbi.v5i2.823

Refbacks

There are currently no refbacks.

BIOPROPAL Industri

Published by :

Institute for Industrial Research and Standardization (Baristand Industri) in Pontianak

Agency for Industrial Research and Development, Ministry of Industry

Jl. Budi Utomo No. 41 Pontianak, West Kalimantan, Indonesia

Tel / Fax : +62 561 881393, 881533

email : biopropal.industri@gmail.com

BIOPROPAL Industri indexed in: